Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳醛树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了醛树脂基活炭制备方法、能及其应用进展和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了用化木材制备醛树脂技术,并对其能进行分析。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型醛树脂是铸造用聚氨酯剂主要成份之一,它结构及成工艺条件决定了该剂能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯与甲醛在碱条件下经加成、缩制得可发醛树脂，该树脂和表面活剂、发泡剂、固化剂一起发泡即得醛泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固醛树脂固化过程,首先是羟甲基发生缩反应,缩反应形成醚键是主要。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳改树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了树脂基活炭制备方法、能及其应用进展和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了用化木材制备树脂技术,并对其能进行分析。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型树脂是铸造用聚氨酯合剂主要成份之一,它结构及合成工艺条件决定了合剂能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯与甲在碱条件下经加成、缩合制得可发树脂，树脂和表面活剂、发泡剂、固化剂一起发泡即得泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固树脂固化过程,首先是羟甲基发生缩合反应,缩合反应形成醚键是主要。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性酚醛树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了酚醛树脂基活性炭制备方法、性能及其应进展和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了酚化木材制备酚醛树脂技术,并对其性能进行分析。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型酚醛树脂是铸造聚氨酯粘合剂主要份之一,它结构及合工艺条件决定了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯酚与甲醛在碱性条件下、缩合制得可发性酚醛树脂，该树脂和表面活性剂、发泡剂、固化剂一起发泡即得酚醛泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性酚醛树脂固化过程,首先是羟甲基发生缩合反应,缩合反应形醚键是主要。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了脂基活性炭制备方法、性能及其应用进展和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了用化木材制备脂技,其性能进行分析。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型脂是铸造用聚氨酯粘合剂主要成份之一,它结构及合成工艺条件决定了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯与甲在碱性条件下经加成、缩合制得可发性脂，该脂和表面活性剂、发泡剂、固化剂一起发泡即得泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性脂固化过程,首先是羟甲基发生缩合反应,缩合反应形成醚键是主要。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用、羧基、、吡四种胶乳改性酚树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了酚树脂基活性炭制备方法、性能及其应用进展和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了用酚化木材制备酚树脂技术,并对其性能进行分析。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

醚型酚树脂是铸造用聚氨酯粘合剂主要成份之一,它结构及合成工艺条件决定了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

酚与碱性条件下经加成、缩合制得可发性酚树脂，该树脂和表面活性剂、发泡剂、固化剂一起发泡即得酚泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性酚树脂固化过程,首先是羟基发生缩合反应,缩合反应形成醚键是主要。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性酚醛树。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

了酚醛树基活性炭制备方法、性能及其应用进展和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了用酚化木材制备酚醛树技术,并对其性能进行分析。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型酚醛树是铸造用聚氨酯粘合剂主要成份之一,它结构及合成工艺条件了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯酚与甲醛在碱性条件下经加成、缩合制得可发性酚醛树，该树和表面活性剂、发泡剂、固化剂一起发泡即得酚醛泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性酚醛树固化过程,首先是羟甲基发生缩合反应,缩合反应形成醚键是主要。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性酚醛树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了酚醛树脂基活性炭制备方法、性能及其应用进展和主方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文了用酚化木材制备酚醛树脂技术,并对其性能进行分析。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型酚醛树脂用聚氨酯粘合剂主成份之一,它结构及合成工艺条件决定了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯酚与甲醛在碱性条件下经加成、缩合制得可发性酚醛树脂，该树脂和表面活性剂、发泡剂、固化剂一起发泡即得酚醛泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性酚醛树脂固化过程,首先羟甲基发生缩合反应,缩合反应形成醚键主。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性酚醛树脂。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了酚醛树脂基活性炭备方法、性能及其应用进展和主要研究方向。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

本文研究了用酚化木材备酚醛树脂技术,并对其性能进行分析。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型酚醛树脂是铸造用聚氨酯粘剂主要成份之一,它结构及成工艺条件决定了该类粘剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯酚与甲醛在碱性条件下经加成、得可发性酚醛树脂，该树脂和表面活性剂、发泡剂、固化剂一起发泡即得酚醛泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性酚醛树脂固化过程,首先是羟甲基发生反应,反应形成醚键是主要。

Phenolic resin was modified respectively using four latexes of butyronitrile-butadiene,carboxylic butyronitrile-butadiene,styrene-butadiene and pyridine-butadiene.

采用丁腈、羧基丁腈、丁苯、丁吡四种胶乳改性酚。

This paper summarizes the preparation method, performance, progress of application and direction of studying phenolic resin acticarbon.

概述了酚基活性炭制备法、性能及其应用进展和主要研究。

The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.

文研究了用酚化木材制备酚技术,并对其性能进行分析。

Benzylic ether phenolic resin is one of the main components of foundry polyurethane binder; its structure and preparation condition determine the performances of polyurethane binder.

苯醚型酚是铸造用聚氨酯粘合剂主要成份之一,它结构及合成工艺条件决定了该类粘合剂性能。

A foamable phenolic resin was prepared,through addition,condensation,in the presence of alkali.The resin was foamed with surfactant, foamer,solidifying agent , then the foam phenolplast was given .

苯酚与甲在碱性条件下经加成、缩合制得可发性酚，该和表面活性剂、发泡剂、固化剂一起发泡即得酚泡沫塑料。

It was shown that the curing process of resoles, at first, proceeded by condensation reaction of methylol groups, and the formation of dimethylene ether linkage was predominant.

结果表明热固性酚固化过程,首先是羟甲基发生缩合反应,缩合反应形成醚键是主要。